Advanced Composites BJ4H-CS BDX
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Advanced Composites, Inc. |
| Trademark: | Advanced Composites |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q72yzq_Advanced-Composites-BJ4H-CS-BDX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Advanced Composites BJ4H-CS BDX is a polypropylene product,. It is available in North America. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.90 - 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 15.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus 3 | 720 | MPa | ASTM D790 |
| Flexural Strength 4 | 18.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -29°C | 480 | J/m | ASTM D256 |
| 23°C | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 67.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 | °C | |
| Middle Temperature | 179 - 199 | °C | |
| Front Temperature | 204 | °C | |
| Nozzle Temperature | 193 | °C | |
| Processing (Melt) Temp | 185 - 227 | °C | |
| Mold Temperature | 26.7 - 43.3 | °C | |
| Injection Rate | Slow-Moderate | ||
| Cushion | 5.00 - 10.0 | mm |
| Injection instructions |
|---|
| Injection Pressure: 20 to 60% of machine capacityScrew RPM: 1 to 2 secs before mold open |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 13 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cariflex® IR0401 BU | Kraton Polymers LLC | IR | Cariflex® |
| Hostaform® EC140CF10 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Latamid 6 H2 G/30-V0HF1 | LATI S.p.A. | Nylon 6 | Latamid |
| LNP™ THERMOCOMP™ MF008S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| Sylvin 3250-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |