Celstran® PA6-GF40-03
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q6htmS_Celstran-PA6-GF40-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% long fiber glass reinforced, heat and UV stabilized, Nylon 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 205 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 325 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 26 | kJ/m² | ISO 179/1eA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 265 - 275 | °C | |
| Middle Temperature | 270 - 275 | °C | |
| Front Temperature | 275 - 280 | °C | |
| Nozzle Temperature | 275 - 280 | °C | |
| Processing (Melt) Temp | 270 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 275 to 280°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOCOMP® PA66 GF40 TS0 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| Eltex® P RF110 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | Eltex® P |
| EPO-TEK® 383ND-LH Premium | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hostacom BJ 49 E NERO | LyondellBasell Industries | PP Copolymer | Hostacom |
| LG ASA LI941 | LG Chem Ltd. | ASA | LG ASA |