TOTAL Polyethylene Lumicene® M 6012 EP
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q5Wh34_TOTAL-Polyethylene-Lumicene-M-6012-EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M6012 EP is a metallocene High Density homopolymer Polyethylene designed to have High Water Vapour Barrier (low WVTR). Lumicene® mPE M6012 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control. The outstanding Water Vapour Barrier gives a significant down-gauging potential for some applications as dry food packaging. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 27.5 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 31.5 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 52.5 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 52.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 870 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 1000 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 55 | g | ISO 7765-1 |
| Water Vapor Transmission 1 | 1.6 | g/m²/24 hr | ASTM E96 |
| Elmendorf Tear Strength | ISO 6383-1 | ||
| MD | 8.0 | kN/m | ISO 6383-1 |
| TD | 28.0 | kN/m | ISO 6383-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 134 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm) | 54 | ASTM D2457 | |
| Haze (40.0 µm) | 15 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 230 | °C |
| Extrusion instructions |
|---|
| BUR: 1.5:1 to 4.5:1Die Gap: 0.8 to 2.8 mmLaboratory test specimens produced with the following extrusion conditions: 45 mm screw diameter, L/D = 30, die diameter = 120 mm, die gap = 1.4 mm, BUR = 2.5:1, temperature = 210°C. |
| Note Message | |
|---|---|
| 1 . | 35 µm, 38 °C, 90% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA6G50HSL-BK10 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| POLYMAN® (SAN) 24/5 | A. Schulman Europe | SAN | POLYMAN® |
| THERMOLAST® K TF5CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Innothane® FM-2046 | Innovative Polymers, Inc. | TSU | Innothane® |
| LNP™ LUBRICOMP™ RX05050 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |