4PROP® 5C20800
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4PROP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q4GFCg_4PROP-5C20800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PROP 5C20800 is a MFI 15 to 24 Recycled Copolymer Polypropylene |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.50 - 0.60 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 15 - 25 | g/10 min | ISO 1133 |
| Density- Annealed | 905 | kg/m³ | ISO 1872 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1300 | MPa | ISO 527-2/5 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 24.0 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 28.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 50 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 1050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 88.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 67.0 | °C | ISO 306/B |
| Melting Temperature 2 | 165 | °C | ISO 11357 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 400 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 20 - 60 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIREX GP5250 | Formosa Plastics Corporation | PS (GPPS) | TAIRIREX |
| Nypol® PA A3 G20 V10 PRTA010 NR302 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Evoprene™ LF 6158 | AlphaGary | SBC | Evoprene™ LF |
| EUROPLEX® Sheet PPSU 99460 | Evonik Industries AG | PPSU | EUROPLEX® Sheet |
| Rotuba CAB B9024 (22% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |