Order Products : sales@su-jiao.com
Hostaform® MT12U03
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q3754u_Hostaform-MT12U03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostaform® MT12U03 is a special grade developed for medical industry applications containing low residual monomers and no animal products. Hostaform® MT12U03 is a moderately high flow grade for faster cycling and thin walled injection molding with improved stiffness and hardness compared to Hostaform® MT12U01. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.8 | % | ISO 294-4 |
| Flow direction | 2.0 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.65 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 20 | % | ISO 527-2/1A/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2750 | MPa | ISO 899-1 |
| 1000 hr | 1450 | MPa | ISO 899-1 |
| Flexural Modulus (23°C) | 3000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 120 | kJ/m² | ISO 179/1eU |
| 23°C | 120 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 112 | °C | ISO 75-2/A |
| Melting Temperature 1 | 170 | °C | ISO 11357-3 |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 190 - 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 210°CZone 4 Temperature: 190 to 210°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zetpol® 3610 | Zeon Chemicals L.P. | NBR | Zetpol® |
| 3M™ Dyneon™ Fluoroplastic THV 610GZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| EMERGE™ PC 4330ECO | Trinseo | PC | EMERGE™ |
| Hostacom BC142/1AC | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ THERMOCOMP™ RZ006SXP compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |