LNP™ VERTON™ MV00ASXP compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q35vPc_LNP-VERTON-MV00ASXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. Also known as: LNP* VERTON* Compound MFX-700-10 HS Product reorder name: MV00ASXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10400 | MPa | ASTM D638 |
| -- | 13900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 131 | MPa | ASTM D638 |
| Break | 141 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.9 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9340 | MPa | ASTM D790 |
| -- | 11100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 187 | MPa | ASTM D790 |
| -- | 214 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.34 | ||
| vs. Itself - Static | 0.52 | ||
| Wear Factor - Washer | 73.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| 23°C 2 | 29 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 66 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.0 | J | ASTM D3763 |
| -- | 13.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 157 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 160 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 221 to 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers PP 30 0100 GF40 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| Network Polymers SMMA MS 125 | Network Polymers, Inc. | Acrylic (SMMA) | Network Polymers SMMA |
| EXCELLOY CK10G10 | Techno Polymer Co, Ltd. | PC+ABS | EXCELLOY |
| IZTAVIL P-1069 | Mexichem Corporativo | PVC Homopolymer | IZTAVIL |
| DEXFLEX® 711-300 BLK | LyondellBasell Industries | TPO (POE) | DEXFLEX® |