Luran® S 757G
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Styrolution |
| Trademark: | Luran® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q31MoW_Luran-S-757G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Luran S 757G provides the best flowability within the product line and is therfore in particular suitable for demanding injection molding geometries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.90 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.7 | % | |
| Equilibrium, 23°C, 50% RH | 0.35 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 51.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.3 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2200 | MPa | |
| 1000 hr | 1650 | MPa | |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | 8.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 97.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 to 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Constant (100 Hz) | 3.40 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 | ||
| 1 MHz | 0.025 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4PROP® 9D11420 H | 4Plas | PP Homopolymer | 4PROP® |
| CERTENE™ LDF-120J | Muehlstein | LDPE | CERTENE™ |
| Clearblend® 155 | Styrolution | MMBS | Clearblend® |
| ENGAGE™ 8540R | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| MAXAMID™ PA66G13HSL-NC010 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |