SABIC® HDPE FI0644
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q2u9Um_SABIC-HDPE-FI0644.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE FI0644 is a high molecular high density polyethylene copolymer grade specifically desinged for blown film applications. SABIC® HDPE FI0644 features are outstanding toughness and impact properties with very low gel level. Application SABIC® HDPE FI0644 is recommended for blown film extrusion. It can be used for producing heavy duty bags, grocery sacks, shopping bags, carier- and T-shirt bags, refuse bags, liners for multi-wall sacks and liners for frozen food meat. The grade is suitable to blend with LLDPE and LDPE and can be used in co-extrusion process. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.944 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 5.4 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.18 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ISO 868 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm | 50.0 | MPa | ISO 527-3 |
| TD : Yield, 20 µm | 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 20 µm | 400 | % | ISO 527-3 |
| TD : Break, 20 µm | 450 | % | ISO 527-3 |
| Dart Drop Impact (20 µm) | 260 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 73.0 | °C | ISO 306/B |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 6383-2 | ||
| MD : 20.0 µm | 200.0 | kN/m | ISO 6383-2 |
| TD : 20.0 µm | 400.0 | kN/m | ISO 6383-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 225 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ST0120-0020 ESD FR Black | PolyOne Corporation | TPU, Unspecified | Stat-Tech™ |
| TAROPRENE® 1 A70 M6N V0 | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Generic PC+Acrylic | Generic | PC+Acrylic | Generic |
| Sylvin 5132-86 Clear Yellow 4174 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ RFL36 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |