AKROMID® B3 GFM 10/20 1 L black (4679)
| Category: | Nylon 6+PP , Polyamide 6 + PP |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q2GeDu_AKROMID-B3-GFM-10-20-1-L-black-4679-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GFM 10/20 1 L black (4679) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide-blend with a reduced density compared to standard PA6 GF10 + M20 Applications are mainly optical components in the automotive and electronic industry, where a weight and cost reduction is required |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 156 | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 30 | % | ISO 1172 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| 2 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E6809T | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Verolloy B5722 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| CALP MRP312 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| LNP™ THERMOCOMP™ PFB55 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ THERMOCOMP™ |
| OTECH PVC OW1065 - Wire Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |