Lucky Enpla LGF1100
| Category: | PC , Polycarbonate |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q0cXAr_Lucky-Enpla-LGF1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LGF1100 is a polycarbonate (PC) product that contains 10% glass fiber reinforced materials. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Lucky Enpla LGF1100 applications include electrical/electronic applications and lighting equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 78.5 | MPa | ASTM D638 |
| Flexural Modulus 2 | 3530 | MPa | ASTM D790 |
| Flexural Strength 3 | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Mold Temperature | 90.0 - 110 | °C | |
| Back Pressure | 1.96 - 3.92 | MPa | |
| Screw Speed | 60 - 80 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 290-310°CInjection Pressure (1st Pressure): 700-1200 kg/cm²Injection Pressure (2nd Pressure): 400-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR36BK9022 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Amilan® CM3003G30 | Toray Resin Company | Nylon 66 | Amilan® |
| INSTRUC POMCGF10 | Infinity LTL Engineered Compounds | Acetal (POM) Copolymer | INSTRUC |
| Karina BLUE PVC COMPOUND 900D06/366-B-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| JSR EPR EP941P | JSR Corporation | EPDM | JSR EPR |