Stirolan PS1
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Stirolan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q0Ymvl_Stirolan-PS1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact resistant polystyrene, for general purpose, with very high MFI, suitable for the injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 28.0 | MPa | |
| Break | 25.0 | MPa | |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 3 | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 52.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 40 | J/m | |
| 23°C, 3.20 mm | 70 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 78.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 84.0 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (1 MHz) | 2.50 | IEC 60250 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 35.NA | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| SCHULAMID® 6 MKF 3010 H | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Sylvin 8240-73 Orange 595 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unilex™ UP 9035-I | United Polychem | PP Impact Copolymer | Unilex™ |
| Nylene® 2415 HSSP BK | Custom Resins Group | Nylon 6 | Nylene® |