Quadrant EPP ERTALON® 4.6 is a Polyamide 46 (Nylon 46) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 3.00 mm | 1.3 | -- | % | |
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.8 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 3.00 mm 1 | 2.6 | -- | % | |
| 23°C, 3.00 mm 2 | 180.0 | -- | mg | |
| 23°C, 3.00 mm 3 | 90.0 | -- | mg |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Service Temperature - Minimum | -40 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale, 10.0 mm) | 92 | -- | ISO 2039-2 | |
| Ball Indentation Hardness (10.0 mm) | 165 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3300 | 1300 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Yield) | 100 | 55.0 | MPa | ISO 527-2/1B/20 |
| Tensile Strain (Break) | 25 | > 100 | % | ISO 527-2/1B/20 |
| Tensile Creep Modulus (1000 hr) | 22.0 | 7.50 | MPa | ISO 899-1 |
| Compressive Stress | ISO 604/1 | |||
| 5% Strain | 94.0 | -- | MPa | |
| 2% Strain | 45.0 | -- | MPa | |
| 1% Strain | 23.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact Strength | 8.0 | 25 | kJ/m² | ISO 180/2A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 160 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature | ||||
| -- 4 | 135 | -- | °C | |
| -- 5 | 155 | -- | °C | |
| -- 6 | 200 | -- | °C | |
| Melting Temperature (DSC) | 295 | -- | °C | |
| CLTE - Flow | ||||
| 23 to 60°C | 8.0E-5 | -- | cm/cm/°C | |
| 23 to 100°C | 9.0E-5 | -- | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.30 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | > 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm, in Oil) | 25 | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.80 | 7.40 | ||
| 1 MHz | 3.40 | 3.80 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 9.0E-3 | 0.13 | ||
| 1 MHz | 0.019 | 0.060 | ||
| Comparative Tracking Index | 400 | 400 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 3.00 mm | HB | -- | ||
| 6.00 mm | HB | -- | ||
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | Weight, 96 hrs |
| 3 . | Weight, 24 hrs |
| 4 . | 20000 hrs |
| 5 . | 5000 hrs |
| 6 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH731 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| TABOND 2001 | SILON s.ro | EVA | TABOND |
| KRALASTIC® GA-704 | Nippon A&L Inc. | ABS | KRALASTIC® |
| Hostaform® C 9021 K | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Hyundai EP Adhesives VE750S/1002 | HYUNDAI EP Co., Ltd. | EVA | Hyundai EP Adhesives |