TECHNIACE® TB-1801
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | TECHNIACE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PzqqGl_TECHNIACE-TB-1801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNIACE® TB-1801 is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) material. It is available in Asia Pacific or North America for injection molding. Primary attribute of TECHNIACE® TB-1801: Heat Resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.09 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/10.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 31 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 83.0 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 9.0E-5 | cm/cm/°C | JIS K7197 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | > 3.0 | hr | |
| Rear Temperature | 230 to 270 | °C | |
| Middle Temperature | 230 to 270 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® 25 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Catalyst LV/1 | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| CompaMid® PA 6.6 HI | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| Lucky Enpla LAY3003R | Lucky Enpla Co LTD | PC+PBT | Lucky Enpla |
| PALMID® R 6 E | pal plast GmbH | Nylon 6 | PALMID® |