Ferro PP NPP00GT03BK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pzhemk_Ferro-PP-NPP00GT03BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ferro PP NPP00GT03BK is a polypropylene material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of Ferro PP NPP00GT03BK are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.7 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 50 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 1160 | MPa | ASTM D790 |
| Tangent : 23°C | 1240 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 37.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 960 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 16.9 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 87.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 51.7 | °C | ASTM D648 |
| RTI Elec (3.18 mm) | 65.0 | °C | UL 746 |
| RTI Imp (3.18 mm) | 65.0 | °C | UL 746 |
| RTI (3.18 mm) | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance | 136 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) | 13.0 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) | 53 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.35 mm) | V-2 | UL 94 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index was tested in accordance with ASTM D3638.California Furniture Testing, TB 133: Passed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 FRM 1 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Devcon High Performance Backing Compound | Devcon | Epoxy | Devcon |
| KOPA® KN333G25BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Hostacom RTA3184 | LyondellBasell Industries | TPO (POE) | Hostacom |
| Leona™ 14G50 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |