Nycast Nymetal 6MPB
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Cast Nylons Ltd. |
| Trademark: | Nycast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PzNH6G_Nycast-Nymetal-6MPB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cast Nylons Ltd., the largest independently-owned North American manufacturer of cast nylon, has combined the best of both worlds - cast nylon and metal - to produce its NYMETAL™ composite. NYMETAL billets made exclusively with NYCAST® nylon and a variety of metal cores, are available for use in manufacturing gears, rollers, and sprockets primarily for power transmission. By combining the performance advantages of nylon and metal into one cohesive unit, NYMETAL offers advantages that cannot be obtained from traditional all metal or all nylon components. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 - 1.16 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.50 - 0.60 | % | ASTM D570 |
| Saturation | 5.0 - 6.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 - 115 | ASTM D785 | |
| Durometer Hardness (Shore D) | 76 - 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2590 - 3030 | MPa | ASTM D638 |
| Tensile Strength | 66.9 - 74.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 - 35 | % | ASTM D638 |
| Flexural Modulus | 2280 - 2410 | MPa | ASTM D790 |
| Flexural Strength | 82.7 - 89.6 | MPa | ASTM D790 |
| Compressive Modulus | 1930 - 2380 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 86.2 - 104 | MPa | ASTM D695 |
| Shear Strength | 68.9 - 75.8 | MPa | ASTM D732 |
| Deformation Under Load | 1.00 - 2.00 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 44 - 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 204 - 221 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.3 - 204 | °C | ASTM D648 |
| Continuous Use Temperature | 110 | °C | |
| Melting Temperature | 227 - 238 | °C | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Service Temperature - Intermittent | 166 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 - 24 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.70 | ASTM D150 | |
| 1 kHz | 3.70 | ASTM D150 | |
| 100 kHz | 3.70 | ASTM D150 |
| Additional Information |
|---|
| The test method for Max. Continuous Use Temp., ASTM D794, was unspecified by the manufacturer.The properties for Nycast 6MPB are based on the average of a range of values provided by the manufacturer. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® 3007C Opaque | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| LGSTRENE LGH 310 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGSTRENE |
| LUVOCOM® 20-8261 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| Hostacom EKC 133N C11498 | LyondellBasell Industries | PP Copolymer | Hostacom |
| PENTAMID B GV30 H UV natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |