Clearflex® H&T LGH 138
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PyqrAu_Clearflex-H-T-LGH-138.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex H&T LGH 138 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, slip agent, antiblocking and processing aid, suitable for blown film extrusion. Films obtained from Clearflex H&T LGH 138 show excellent optical properties, a wide sealing window, both hot tack and heat seal, together with a low sealing initiation temperature (S.I.T.) and outstanding impact, puncture and Elmendorf tear resistance. Main Application Clearflex H&T LGH 138, for its overall characteristics, is the right choice for packaging film applications requiring superior mechanical and optical properties. The excellent sealability behaviour together with low gel content makes it ideal for lamination film production. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.11 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 160 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 170 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| TD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| MD : Break, 25 µm, Blown Film | 40.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 40.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 450 | % | |
| TD : Break, 25 µm, Blown Film | 700 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 350 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 110.0 | kN/m | |
| TD : 25.0 µm | 200.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ISO 306/A |
| Melting Temperature | 117 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 11 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESN P10 TL | Arkema | Nylon 11 | Rilsan® |
| RTP ESD C 2800-90A | RTP Company | TPO (POE) | RTP |
| Dynacom 702 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| Sumiliteresin® PR-53416 | SBHPP | Phenolic | Sumiliteresin® |
| 3M™ Dyneon™ PTFE Compound PDR 08004 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |