EPO-TEK® 323LP
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pym3Gd_EPO-TEK-323LP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® 323LP is a two component, high temperature epoxy designed for semiconductor, hybrid, fiber optic, and medical applications. It is a longer pot life alternative of EPO-TEK® 353ND and is also available in a single component, frozen syringe. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 100 | °C | |
| CLTE - Flow | |||
| -- 2 | 3.1E-5 | cm/cm/°C | |
| -- 3 | 1.3E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.570 | ||
| Transmittance | |||
| 640 to 800 nm | > 90.0 | % | |
| 820 to 1620 nm | > 94.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 413 | °C | |
| Die Shear Strength - >20 kg (23°C) | 46.9 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus | 2.67 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.31 | % | |
| 250°C | 0.46 | % | |
| 300°C | 0.85 | % |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 5 | Clear/Transparent | ||
| -- 6 | Yellow | ||
| Density | |||
| Part B | 1.09 | g/cm³ | |
| Part A | 1.20 | g/cm³ | |
| Viscosity 7(23°C) | 3.5 to 5.0 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 1400 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 88 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 2.62 | ||
| Volume Resistivity (23°C) | > 3.0E+12 | ohms·cm | |
| Dissipation Factor (1 kHz) | 3.2E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part A |
| 6 . | Part B |
| 7 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4005 | RTP Company | PPA | RTP |
| Starflam RF0023P | Eurostar Engineering Plastics | Nylon 66/6 | Starflam |
| Formolon® 614 | Formosa Plastics Corporation, U.S.A. | PVC, Rigid | Formolon® |
| LEXAN™ ML9103R resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Sylvin 9077-70 Blue 8401 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |