OnForce™ LFT 5200-5001 FR Natural
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnForce™ LFT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pygcs0_OnForce-LFT-5200-5001-FR-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.25 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Flexural Modulus | 10200 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 30 | kJ/m² | ISO 179 |
| Dart Drop Impact | 14.0 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 154 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 140 | °C | ISO 75-2/C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (3.20 mm) | V-0 | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 210 - 230 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 1.00 | MPa |
| Injection instructions |
|---|
| LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed. |
| Note Message | |
|---|---|
| 1 . | Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processingconditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP525-283UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Ad-Tech Epoxy EC-413 Medium | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Axpoly® r-PP51 1000 | Axion Polymers | PP Copolymer | Axpoly® |
| DENKA POVAL W-100 | Denka Company Limited | PVOH | DENKA POVAL |
| Europrene® 1723 | Versalis S.p.A. | SBR, Emulsion | Europrene® |