Pearlthane® 11T95P
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PyT4qM_Pearlthane-11T95P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlthane® 11T95P is a polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, combining hardness with excellent mechanical properties. A special additive package assures excellent paintability of injection moulded parts. Pearlthane® 11T95P is recommended for injection moulding applications, such as: seals, wheels and castors, ear-tags, shoe soles and a variety of high performance technical parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| 20°C | 1.19 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 95 | ASTM D2240, ISO 868 | |
| Shaw D | 49 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 12.0 | MPa | ASTM D412, ISO 527 |
| 300% strain | 25.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 500 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 135 | kN/m | ASTM D624 |
| -- | 140 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 32 | % | ASTM D395B |
| 70°C, 22 hr | 42 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -38.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 195 - 205 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 195 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 210 | °C | |
| Mold Temperature | 35.0 | °C |
| Injection instructions |
|---|
| Closing force: : 30 tonsScrew diameter: : 30 mmMaximum hydraulic pressure: : 210 barMould: : Plaque120x120x2 mmL/D ratio: : 23 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 40YM240 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| RheTech Thermoplastic Polyolefin FT1055-685UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| NYCOA Polyamide 5300 ST | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| LOTTMER HX-075AB | Lotte Chemical Corporation | TPE | LOTTMER |
| PolyFibra® PF-PHF04 | FuturaMat | PP, Unspecified | PolyFibra® |