EMOPLEN® CP FR V0
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | EMAS Plastik San.Tic.AS. |
| Trademark: | EMOPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pxrnaw_EMOPLEN-CP-FR-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer V0 flammability |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 - 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 - 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.3 - 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 - 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 - 3500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | > 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 20 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 160 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | VDE 0471/2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® CP 2002 | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| DIGITALWAX® DC 550 | DWS Systems | Unspecified | DIGITALWAX® |
| Infino TK-2046HM | SAMSUNG SDI CO., LTD. | PCT | Infino |
| Golden Compound PP S²PC 3545 BO 10LP41 | Golden Compound GmbH | PP, Unspecified | Golden Compound |
| ESTOPLAST XU 150GY64 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |