OXPEKK® MG230C
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | Oxford Performance Materials, Inc. |
| Trademark: | OXPEKK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PxemSl_OXPEKK-MG230C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OXPEKK® MG230C is a Polyetherketoneketone (PEKK) material filled with 30% carbon fiber. It is available in Europe or North America. Typical application of OXPEKK® MG230C: Medical/Healthcare |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ASTM D638 |
| Tensile Strength (Break) | 262 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 291 | MPa | ASTM D790 |
| Compressive Strength | 241 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 321 | °C | ASTM D648 |
| Glass Transition Temperature | 163 | °C | DSC |
| Melting Temperature | 360 | °C | DSC |
| CLTE - Flow | 1.0E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx F663E13 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| NAXALOY® 793MF6 | MRC Polymers, Inc. | PC+Polyester | NAXALOY® |
| NORDEL™ IP 4570 | The Dow Chemical Company | EPDM | NORDEL™ |
| 4DUR® 9K23100 H | 4Plas | PBT | 4DUR® |
| GERMAMID 6 GK 50 | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |