KumhoSunny PET HEG3645
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Px7iyG_KumhoSunny-PET-HEG3645.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEG3645 is a 45% glass fiber reinforced, modified polyethylene terephtalate for injection molding. offering high rigidity,high heat resistance, good surface quality and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.71 | g/cm³ | ASTM D792 |
| -- | 1.75 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.50 | % | ASTM D955 |
| -- | 0.40 to 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 162 | MPa | ASTM D638 |
| -- | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 16000 | MPa | ASTM D790 |
| -- 1 | 12000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 220 | MPa | ASTM D790 |
| -- 2 | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Notched Izod Impact | |||
| 3.20 mm | 90 | J/m | ASTM D256 |
| 23°C | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 255 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 240 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 3 | 230 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 245 to 260 | °C | |
| Middle Temperature | 250 to 265 | °C | |
| Front Temperature | 255 to 270 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Processing (Melt) Temp | 245 to 275 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WanBlend® WHT-HF8685 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| VALOX™ HX3061HP resin | SABIC Innovative Plastics | PBT | VALOX™ |
| Casico™ FR4807 | Borealis AG | Polyolefin, Unspecified | Casico™ |
| LUVOCOM® 1-8379 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Pearlbond™ 100 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |