Generic PP Homopolymer - Glass Fiber, Long
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PwnYG5_Generic-PP-Homopolymer---Glass-Fiber-Long.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Glass Fiber, Long This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.03 - 1.48 | g/cm³ | ASTM D792 |
| 23°C | 1.12 - 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.12 - 0.40 | % | ASTM D955 |
| 23°C | 0.17 - 0.33 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 6090 - 13100 | MPa | ASTM D638 |
| 23°C | 6240 - 13300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 90.0 - 140 | MPa | ASTM D638, ISO 527-2 |
| Fracture, 23°C | 105 - 131 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 1.5 - 2.6 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4340 - 11200 | MPa | ASTM D790 |
| 23°C | 6250 - 13000 | MPa | ISO 178 |
| Flexural Strength (23°C) | 155 - 230 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 - 30 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 54 - 76 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 100 - 350 | J/m | ASTM D256 |
| 23°C | 18 - 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 149 - 165 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 - 159 | °C | ISO 75-2/A |
| Melting Temperature | 167 - 168 | °C | ISO 11357-3, ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 93.3 | °C | |
| Processing (Melt) Temp | 216 - 225 | °C | |
| Mold Temperature | 54.7 - 65.8 | °C | |
| Back Pressure | 0.259 - 1.00 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Glass Fiber, LongThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALEN™ PPH327G28 | SAX Polymers | PP Homopolymer | SAXALEN™ |
| Sylvin 7607-90 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vi-Chem PVC V142-90 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| EVERLON® TA-65 | Ever Polymer Co., Ltd. | SEBS | EVERLON® |
| Geon™ Vinyl Dry Blend E7755 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |