UBE Nylon P7115 U
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBE Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pwfbkh_UBE-Nylon-P7115-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBESTA P7115 U is a low viscosity, non-reinforced and non-plasticized Polyamide 12/6 copolymer powder. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/1.0 kg) | 34 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.6 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.4 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 66 | ISO 2039-2 | |
| Durometer Hardness (Shore D) | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | ISO 527-2 |
| Fracture | 300 | % | ISO 527-2 |
| Flexural Modulus | 500 | MPa | ISO 178 |
| Flexural Stress | 22.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, complete fracture | 1.0 | kJ/m² | ISO 179/1eA |
| 23°C, complete fracture | 11 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 47.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 42.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 145 | °C | ISO 3146 |
| CLTE - Flow | 1.7E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >300%Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 5 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S610 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Zhongfa PBT G-20V | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PBT | Zhongfa |
| AKROMID® S3 GF 30 1 black (3259) | AKRO-PLASTIC GmbH | Nylon 610 | AKROMID® |
| Latilub 80-10T G/40 | LATI S.p.A. | PPS | Latilub |
| Softell TKG 317N C12616 | LyondellBasell Industries | PP Copolymer | Softell |