Nypol® PA A3 G25 NTLA010 NR342
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PwN2SE_Nypol-PA-A3-G25-NTLA010-NR342.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 25% fiberglass, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.32 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 1.1 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 2.0 | -- | % | ASTM D570 |
| Ash Content | 23 to 27 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Break) | 180 | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 7.0 | % | ASTM D638 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (Area) | ASTM D256 | |||
| -30°C | 7.00 | 7.00 | kJ/m² | |
| 27°C | 10.0 | 11.0 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | |||
| -30°C | 60.0 | 45.0 | kJ/m² | |
| 27°C | 60.0 | 80.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 261 | -- | °C | |
| 1.8 MPa, Unannealed | 252 | -- | °C | |
| Vicat Softening Temperature | 257 | -- | °C | ASTM D1525 1 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| CLTE | ASTM D696 | |||
| Flow : 23 to 55°C | 1.1E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 3.3E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 | -- | ohms·cm | ASTM D257 |
| Relative Permittivity (100 Hz) | 3.60 | -- | IEC 60250 | |
| Dissipation Factor (100 Hz) | 7.0E-3 | -- | ASTM D150 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP CPV340 | Sasol Polymers | PP Impact Copolymer | Sasol Polymers PP |
| VINIKA® CA95KA-1 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Xuchuan XCS-3565C | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| BCC Resins BC 5003 | BCC Products Inc. | Epoxy | BCC Resins |
| Hanwha Total PP TH54M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |