RTP 2285 TFE 15
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PvxWaO_RTP-2285-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. PEEK reinforced with carbon fiber is a advanced thermoplastic composite with excellent properties. Coupled with PTFE gives the compound increased wear capabilities. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.050 - 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 31000 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 159 | MPa | ASTM D638 |
| -- | 234 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.3 | % | ASTM D638 |
| Flexural Modulus | 24100 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 345 | MPa | ASTM D790 |
| Yield | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 288 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | V-0 | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D955, 0.25in: 1 mil/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 357 - 427 | °C | |
| Middle Temperature | 357 - 427 | °C | |
| Front Temperature | 357 - 427 | °C | |
| Mold Temperature | 121 - 204 | °C | |
| Injection Pressure | 82.7 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2950T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Kumho SBR 1712L | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Kazan HDPE 293-2B5D | Kazanorgsintez Joint Stock Company | HDPE | Kazan HDPE |
| TECHNYL® A 216 V15 BLACK 21N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Marlex® HMN TR-945G | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |