EL-Lene™ F15
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PvoOhv_EL-Lene-F15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-LENE F15 is a product of bi-modal process from Mitsui Chemicals, Inc. of Japan. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.060 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 12 µm | 971 | MPa | |
| 2% Secant, TD : 12 µm | 961 | MPa | |
| Tensile Strength | ASTM D882 | ||
| TD : Yield, 12 µm | 31.4 | MPa | |
| MD : Break, 12 µm | 89.2 | MPa | |
| TD : Break, 12 µm | 37.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 350 | % | |
| TD : Break, 12 µm | 530 | % | |
| Dart Drop Impact (12 µm) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 12 µm | 3.0 | g | |
| TD : 12 µm | 140 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Melting Temperature | 130 | °C | ASTM D2117 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMORUN® TT744N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| ALTECH® PA66 A 2035/109 GF35 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| GAPEX® RPP10EA78NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| Kepital® TB-31 | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| LNP™ THERMOTUF™ R1000I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |