| High Viscosity Acetal Homopolymer with Improved Processing |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.6 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.20 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.9 | % | |
| Flow | 2.2 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 1.4 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 88 | ||
| R-Scale | 119 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2950 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 71.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 25 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 45 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2700 | MPa | |
| 1000 hr | 1500 | MPa | |
| Flexural Modulus | 2850 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 77.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 400 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 12 | kJ/m² | |
| 23°C | 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 175 | °C | ISO 306/A50 |
| -- | 160 | °C | ISO 306/B50 |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Flow : -40 to 23°C | 1.0E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 23°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 41 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.012 | ||
| 1 MHz | 5.5E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.19 | g/cm³ |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 8.00 | mg/kg | VDA 275 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Nylon 1013B | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| Badadur® PBT8 GF30 | Bada AG | PBT | Badadur® |
| FERREX® GPP20CF54UL-WH | Ferro Corporation | PP, Unspecified | FERREX® |
| ESTABLEND 6500 GF | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| Karina CLEAR PVC COMPOUND -E 75/2001-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |