3M™ Dyneon™ PTFE Compound TF 4105
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PtGOQO_3M-Dyneon-PTFE-Compound-TF-4105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.24 | g/cm³ | ISO 12086 |
| Apparent Density | 0.82 | g/cm³ | ISO 12086 |
| Average Particle Size | 580 | µm | ISO 12086 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 70.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | 370 to 375 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Break) | 16.0 | MPa | ISO 12086 |
| Tensile Strain 2(Break) | 360 | % | ISO 12086 |
| Deformation Under Load 3(23°C, 15 MPa) | 8.40 | % | ASTM D621 |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | 100 h load, 25 h relaxation |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIVIC® 1100 | SIDIAC | NBR | SIVIC® |
| Thermylene® P-30TC-1156 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| ADDILENE J 522 M20 | ADDIPLAST | PP Copolymer | ADDILENE |
| Latamid SP2 H2 G/45 | LATI S.p.A. | Nylon 612 | Latamid |
| Karina WHITE PVC COMPOUND 800D10/7-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |