LNP™ LUBRICOMP™ RI001 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PtCCSF_LNPLUBRICOMPRI001compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RI001 is a compound based on Nylon 66 resin containing 2% Silicone. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RL-4410 Product reorder name: RI001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.15 | g/cm³ | ASTM D792 |
| -- | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 2.0 - 4.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 - 4.0 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 1.2 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3210 | MPa | ASTM D638 |
| -- | 2930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 61.0 | MPa | ASTM D638 |
| Fracture | 68.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 3.7 | % | ISO 527-2/5 |
| Fracture 3 | 2.6 | % | ASTM D638 |
| Fracture | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 2910 | MPa | ASTM D790 |
| -- 5 | 2690 | MPa | ISO 178 |
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.44 | ASTM D3702 Modified | |
| With Self-Static | 0.27 | ASTM D3702 Modified | |
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.300 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Washer | 104 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 45 | J/m | ASTM D256 |
| 23°C 6 | 5.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 7 | 210 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.10 | J | ASTM D3763 |
| -- | 0.700 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 241 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 8 | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 66.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 59.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 8.3E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® NXT PP-H A 2430/450 GF20 MR10 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® NXT PP-H |
| Enviramid® N2315THL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| Karina WHITE PVC COMPOUND 807-10/236-H-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS EW351 | AD majoris | PP, Unspecified | MAJORIS |
| LEXAN™ 943A resin | SABIC Innovative Plastics | PC | LEXAN™ |