Optix® CP-1000 IG
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Plaskolite, Inc. |
| Trademark: | Optix® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pt2FSq_OptixCP1000IG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Optix®CP-1000 IG is a polymethyl methacrylate-acrylic material,. This product is available in North America or Europe,. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) | 2.7 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength | 42.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 37 | % | ASTM D638 |
| Flexural Strength | 61.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 64 | J/m | ASTM D256 |
| Dart Drop Impact 1(3.18 mm) | 6.33 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 99.4 | °C | ASTM D1525 |
| CLTE - Flow (-30 to 30°C) | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Geometry GB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1310ST | Shin-Etsu Silicones of America | Silicone Rubber, RTV-2 | Shin-Etsu RTV |
| WELLAMID Nylon 6600/50 GV 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Borealis PP RE420MO | Borealis AG | PP Random Copolymer | Borealis PP |
| Cheng Yu FV30720 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Karina WHITE PVC COMPOUND -E 830-10/145-A-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |