Pearlthane® D11H95S
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pt1SEA_Pearlthane-D11H95S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Pearlthane® D11H95S is a high performance polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, featuring excellent flow and mechanical properties and an outstanding low compression set value and high temperature resistance. Product recommended for injection-moulding applications with an extremely short cycle time. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| 20°C | 1.19 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 29.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 94 | ASTM D2240, ISO 868 | |
| Shaw D | 45 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 13.0 | MPa | ASTM D412, ISO 527 |
| 300% strain | 25.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 47.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 480 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 169 | kN/m | ASTM D624 |
| -- 2 | 170 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 18 | % | ASTM D395B |
| 70°C, 22 hr | 23 | % | ASTM D395B |
| 100°C, 70 hr | 36 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 3 | -38.0 | °C | ISO 11357-2 |
| Melting Temperature 4 | 215 - 225 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 200 | °C | |
| Middle Temperature | 205 | °C | |
| Front Temperature | 205 | °C | |
| Nozzle Temperature | 210 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing Force: 30 tonsScrew Diameter: 30 mmMaximum Hydraulic Pressure: 210 barMould: Disc 50x50x6 mm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Method B |
| 3 . | 10°C /min. |
| 4 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 2862-60A | RTP Company | TPO (POE) | RTP |
| Gallonprene® GP540-8001(n)F | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Gallonprene® GP310-7502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kuraray Poval® PVA 420H | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| KMI PP KM-013BB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |