TAIRILOY AC2500
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRILOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pryeao_TAIRILOY-AC2500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC PC/ABS resin AC2500 meets the requirements of SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.14 | g/cm³ | ASTM D792 |
| 23°C | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 7.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class R, 23°C | 110 | ASTM D785 | |
| R scale, 23°C | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 52.0 | MPa | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 2450 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 89.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 3.18 mm) | 570 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 103 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 132 | °C | ISO 306/A, ASTM D1525 1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 220 - 250 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Die Temperature: 230 to 270°CInjection Volume: 30 to 80% of injection machine's capacity |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNAB® EM60 | Tyne Plastics LLC. | ABS | TYNAB® |
| Celcon® LW90-F2 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| ESTOPLAST XU 6100 NN01 | Ester Industries Ltd. | Nylon, Unspecified | ESTOPLAST XU |
| Elastollan® 1264 D U | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| KOCETAL® K300LOBBN | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |