ExxonMobil™ LLDPE LL 6407.67
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Prmsh6_ExxonMobil-LLDPE-LL-6407-67.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LL 6407 is an ethane copolymer with narrow molecular weight distribution, developed for applications with excellent environmental stress cracking resistance requirements. The resin has good processability, minimum warpage and excellent toughness suitable for low temperature durability. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.8 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, F50) | 238 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 17.5 | MPa | ASTM D638 |
| Flexural Modulus | ASTM D790B | ||
| 1% secant | 727 | MPa | ASTM D790B |
| 2% secant | 638 | MPa | ASTM D790B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 112 | °C | ASTM D1525 |
| Peak Melting Temperature | 127 | °C | ASTM D3418 |
| Additional Information |
|---|
| 性能基于注塑成型样本。可以修改测试流程以适应操作条件或设施限制。 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 3700-80NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| DIOSHY® VP-860 | DIOSHY Co.,Ltd. | TPV | DIOSHY® |
| Elastane™ 4762-90A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Geon™ Vinyl Flexible B6DT0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| TechnoFiber PP LGF 30-10-01 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber |