Hanwha Total PP BJ70M
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PreyZc_Hanwha-Total-PP-BJ70M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BJ70M is a heat-resistant/light-stability polypropylene compound containing a base resin with superior impact-resistance for high-impact strength and excellent light-stability, keeping discoloration in ultraviolet light to a minimum. This product is best in lighting components used in high temperature environments. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.4 - 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 27.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 200 | % | ASTM D638 |
| Flexural Modulus 3 | 1320 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 180 - 200 | °C | |
| Nozzle Temperature | 190 - 210 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Pressure | 39.2 - 78.5 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa |
| Injection instructions |
|---|
| Injection Speed: 50 to 80 % |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alathon® H5234 | LyondellBasell Industries | HDPE | Alathon® |
| ALCOM® PA6 900/1 MO1 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Geon™ Vinyl Flexible 1351 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hanwha Total PP HF429 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |
| LNP™ LUBRICOMP™ DX07035 compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |