Ultramid® SEGM35 H1 BK-126
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PrQXW8_Ultramid-SEGM35-H1-BK-126.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G HS BK-106. In parts containing cross sections, significant pressure drops are encountered during filling. Applications Ultramid SEGM35 H1 BK-126 is generally recommended for applications such as mirror housings, rear liftgate handles and luggage rack components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.48 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | -- | % | |
| Water Absorption | ||||
| 24 hr | 0.90 | -- | % | ASTM D570 |
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Saturation | 5.7 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.7 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.6 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.6 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 9210 | -- | MPa | |
| 23°C | 8290 | 3900 | MPa | |
| 80°C | 3310 | 3050 | MPa | |
| 121°C | 2760 | 2320 | MPa | |
| Tensile Strength | ||||
| Break, -40°C | 175 | 153 | MPa | ASTM D638, ISO 527-2 |
| Break, 23°C | 119 | -- | MPa | ASTM D638 |
| Break, 80°C | 58.0 | 46.0 | MPa | ASTM D638, ISO 527-2 |
| Break, 121°C | 49.0 | 38.0 | MPa | ASTM D638, ISO 527-2 |
| Break, 23°C | 119 | 67.0 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, -40°C | 2.9 | 2.6 | % | ASTM D638 |
| Break, 23°C | 2.6 | -- | % | ASTM D638 |
| Break, 80°C | 6.6 | 5.9 | % | ASTM D638 |
| Break, 121°C | 7.6 | 7.3 | % | ASTM D638 |
| Break, 23°C | 2.6 | 5.6 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 7600 | -- | MPa | ASTM D790 |
| 23°C | 7000 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 200 | -- | MPa | ASTM D790 |
| 23°C | 186 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ||||
| 23°C | 53 | -- | J/m | ASTM D256 |
| -40°C | 4.3 | -- | kJ/m² | ISO 180 |
| 23°C | 5.8 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | -- | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP201N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Moplen EP300K | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Chemraz 515 | Greene, Tweed & Co. | PTFE | Chemraz |
| Geon™ Vinyl Flexible XV3765 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Geon™ Vinyl Rigid Extrusion 87555 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |