Arnitel® EM400
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pqn9mA_Arnitel-EM400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnitel®EM400 is a thermoplastic polyester elastomer (TPC-ET) material,. This product is available in North America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Arnitel®The main characteristics of EM400 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Apparent Density | 0.69 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 33.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.5 | % | ISO 294-4 |
| Flow direction | 1.5 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.75 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 33 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 40.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture | 21.0 | MPa | ISO 527-2 |
| 5.0% strain | 2.10 | MPa | ISO 527-2 |
| 10% strain | 3.50 | MPa | ISO 527-2 |
| 50% strain | 6.50 | MPa | ISO 527-2 |
| 100% strain | 7.30 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 830 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | No Break | ISO 179/1eA | |
| 23°C | No Break | ISO 179/1eA | |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | No Break | ISO 180/1A | |
| 23°C | No Break | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 195 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.10 | IEC 60250 | |
| 1 MHz | 4.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.017 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.60 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 205 - 240 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® F FN51000 | LyondellBasell Industries | LDPE | Microthene® F |
| Monprene® RG-20160 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| TKC PS | TKC Kunststoffe e.K. | PS (GPPS) | TKC |
| Elastollan® C 78 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Zytel® PLUS PLS95G35DH1 BK549 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® PLUS |