Ultramid® A3X2G5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PqgaXD_Ultramid-A3X2G5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid A3X2G5 is a 25% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term performance. Flame retardant based on red phosphorus; outstanding mechanical and electrical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.34 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 40.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | -- | % | |
| Water Absorption | ||||
| Saturation | 6.0 | -- | % | ASTM D570 |
| Saturation, 23°C | 6.0 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.4 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8500 | 6000 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 138 | -- | MPa | ASTM D638 |
| Break, -40°C | 196 | -- | MPa | ISO 527-2 |
| Break, 23°C | 140 | 100 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.0 | -- | % | ASTM D638 |
| Break, 23°C | 3.0 | 4.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7100 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 13 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 60 | 65 | kJ/m² | |
| 23°C | 65 | 70 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 64 | -- | J/m | |
| 23°C | 75 | -- | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 238 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 260 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 2.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 3.0E-5 | -- | cm/cm/°C | |
| Transverse | 7.0E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.400 mm | 110 | -- | °C | |
| 0.810 mm | 120 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.400 mm | 115 | -- | °C | |
| 0.810 mm | 115 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 115 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.810 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | 1.0E+13 | 1.0E+10 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index | 550 | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.810 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 285 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 903 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| VITAMIDE® BR14 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Grivory® HT2C-3X black 9833 | EMS-GRIVORY | Nylon 6T/66 | Grivory® |
| Hetron™ FR 998/35 | Ashland Performance Materials | Vinyl Ester | Hetron™ |
| ALCOM® MED PS 1000 04004 | ALBIS PLASTIC GmbH | PS (GPPS) | ALCOM® MED PS |