E-RIALFILL H 07 20 T2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PqPgVB_E-RIALFILL-H-07-20-T2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer obtained by recycling of industrial scrap, 20% talc filled Flowability rate specific for injection molding, good thermal and mechanical characteristics. Available in versions black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 1.1 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Ash Content | 20 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 30.0 | MPa | |
| Break, 23°C | 24.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 5.0 | % | |
| Break, 23°C | 15 | % | |
| Flexural Modulus 2(23°C) | 2600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 2.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 63.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 92.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP HDPE 055952 | Amco Polymers | HDPE | PRIMATOP |
| DURACON® M90-44 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Gallonprene® GP520-7501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Ebalta SG 241 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Hostacom TRC 787N | LyondellBasell Industries | TPO (POE) | Hostacom |