RTP 3281
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PqG1kE_RTP-3281.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- RTP 3281 is a 10% carbon fiber reinforcement ethylene tetrafluoroethylene. This product exhibits excellent heat and chemical resistance along with good wear properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 290 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 850 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 199 | °C | ASTM D648 |
| CLTE - Flow | 5.4E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 8mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 282 - 360 | °C | |
| Middle Temperature | 282 - 360 | °C | |
| Front Temperature | 282 - 360 | °C | |
| Mold Temperature | 65.6 - 149 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Clamp Tonnage | 5.5 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A R 218 V25 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Vinnolit® M 68 FW | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| TRANSMARE® BIO 35MI-10-0.001 | Transmare Compounding B.V. | PLA | TRANSMARE® BIO |
| Bergamid™ B650 G/Mi20 UF | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Kumho SBR 1500 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |