Witcom PEEK 3C/3L1-EM
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PqEOrI_Witcom-PEEK-3C-3L1-EM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PEEK 3C/3L1-EM is a polyetheretherketone (PEEK) product that contains a 15% carbon fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.30 - 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 - 3.0 | % | ISO 527-2 |
| Flexural Modulus | 11500 | MPa | ISO 178 |
| Flexural Stress | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 315 | °C | ISO 75-2/A |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 220 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 180 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 380 - 410 | °C | |
| Mold Temperature | 160 - 200 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.250 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TW341 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Emulprene® 1500A | INSA | SBR, Emulsion | Emulprene® |
| Plexiglas® VOD | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Sumiliteresin® PR-50731 | SBHPP | Phenolic | Sumiliteresin® |
| Sumiliteresin® PR-12603 | SBHPP | Phenolic | Sumiliteresin® |