TAROLON 3002 G3
| Category: | PC , Polycarbonate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PqCCNg_TAROLON-3002-G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate medium high viscosity 15% glass fibres reinforced, flame retardant UL94 V1. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 - 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.080 | % | ISO 62 |
| Saturated, 23°C | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4300 | MPa | ISO 178 |
| Flexural Stress 2 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 153 | °C | ISO 306/A50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-1 | UL 94 | |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 100 - 120 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 120 to 130°CPre-heat Time: 3 hrs |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9739-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Fainplast PVC KL 101/2 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Fenochem T 4700/S | Chemiplastica, Inc. | Phenolic | Fenochem |
| Flexalloy® 9100-75 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Hostacom X M1 T01 105555 | LyondellBasell Industries | PP Copolymer | Hostacom |