Order Products : sales@su-jiao.com
TOTAL Polystyrene Impact 6351
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ppwdp0_TOTAL-Polystyrene-Impact-6351.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Impact 6351 is a high gloss, easy flow polystyrene for injection molding application. It is recommended for manufacturing of articles which require glossy surface and good dimensional stability at elevated temperatures. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| Saturation | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Grade R, 23°C, Injection Molding | 99 | ASTM D785 | |
| R scale, 23°C | 99 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 32.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 55 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 2000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, injection molding | 95 | J/m | ASTM D256 |
| 23°C, injection molding | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/A50, ASTM D1525 1 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Heat Distortion | |||
| -- | 82 | °C | ISO 75-2 |
| -- | 82 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Dielectric Strength | 150 | kV/mm | ASTM D149 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 80 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 150 - 180 | °C | |
| Middle Temperature | 180 - 210 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 250 | °C |
| Injection instructions |
|---|
| Zone 4: 210 - 240 °C |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 2862 | RTP Company | TPO (POE) | RTP |
| TRANSMARE® 14CT40-0.002 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| EPO-TEK® UD1355 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| OmniCarb™ PC/ABS 270 | OMNI Plastics, LLC | PC+ABS | OmniCarb™ |
| LNP™ THERMOCOMP™ PF008 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |