Zytel® 70G33HS1L BK031
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ppai3c_Zytel-70G33HS1L-BK031.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% Glass Reinforced, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.39 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 9300 | -- | MPa | ISO 178 |
| Flexural Stress | 280 | 195 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 10 | -- | kJ/m² | |
| 23°C | 13 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 75 | 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 10 | -- | kJ/m² | |
| 23°C | 12 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 252 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | |
| Transverse | 8.3E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 1 | -- | UL 746 | |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN RPPC711 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| Caltex PP M540S | GS Caltex | PP Impact Copolymer | Caltex PP |
| APEX® 1590 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina BLACK COLOR CONCENTRATE MBU -E 48/ 1-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SIBUR Synthetic Rubber DST-30-01 | SIBUR | SBC | SIBUR Synthetic Rubber |