KOPA® KN333G33
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PpZ43c_KOPA-KN333G33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KOPA® KN333G33 is a Polyamide 66 (Nylon 66) product filled with glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 196 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 6.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9320 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 284 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 250 | °C | |
| 1.8 MPa, Unannealed | 247 | °C | |
| Peak Melting Temperature | 255 | °C | ASTM D3418 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-MFC-101G30 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| TPV Elastoprene® N73A-i | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| XANTAR® C MC 3700 | Mitsubishi Engineering-Plastics Corp | PC+ABS | XANTAR® C |
| Sylvin 8260-85 White 1591 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8994-76 White 1366 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |