ShinkoLite-P MD
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | ShinkoLite-P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PpNNku_ShinkoLite-P-MD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Approved Rating: SAE Unspecified |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ASTM D638 |
| Tensile Strength (Break) | 68.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3040 | MPa | ASTM D790 |
| Flexural Strength (Break) | 103 | MPa | ASTM D790 |
| Compressive Strength | 103 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 88.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| CLTE - Flow | 5.9E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1460 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.70 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.050 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance | 93.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 190 to 240 | °C | |
| Middle Temperature | 190 to 240 | °C | |
| Front Temperature | 190 to 240 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 78.4 to 137 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 to 220 | °C | |
| Cylinder Zone 2 Temp. | 210 to 230 | °C | |
| Cylinder Zone 3 Temp. | 210 to 230 | °C | |
| Die Temperature | 210 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218W V30 BLACK FA | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| MTEGRITY™ LDPE LD500 | M. Holland Company | LDPE | MTEGRITY™ LDPE |
| K-Prene SHEATHING EPR 5064 | Technovinyl Polymers India Ltd. | MPR | K-Prene |
| Plaslube® AC-80/TF/5 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| Sylvin 9067-90 GREY 9132 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |