| 20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.40 | % | |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 0.30 | % | ISO 62 |
| Viscosity Number | 120 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 6500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 8.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 7.0 | kJ/m² | |
| -30°C | 7.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 175 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 110 | °C | ISO 11357-2 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 30 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.17 | g/cm³ | |
| Specific Heat Capacity of Melt | 1900 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.24 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® TS10BK8517 | Jackdaw Polymers | Nylon 66/6 | VITAMIDE® |
| Nipol® DN3635 | Zeon Chemicals L.P. | NBR | Nipol® |
| FHR EPS 54-7354 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Lifolit® E 73.1340/2 glasklar | ELASTO | PVC, Flexible | Lifolit® |
| Polifor® L6 GF/50 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |