ULTEM™ PW2400 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PonVQv_ULTEM-PW2400-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% Glass fiber filled, standard flow Polyetherimide (Tg 217°C). Specific grade-colors are designed and certified for use in Potable Water applications. KTW, WRAS, ACS, NSF-61 and W270 certified. US FDA and European Food Contact approved. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.10 to 0.30 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 10000 | MPa | ISO 178 |
| Flexural Stress | 240 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 20.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 215 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 210 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 230 | °C | ISO 306/A50 |
| -- | 217 | °C | ISO 306/B50 |
| -- | 225 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 150°C | 1.5E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 4.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.33 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 48 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 to 100 | °C | |
| Rear Temperature | 350 to 390 | °C | |
| Middle Temperature | 370 to 410 | °C | |
| Front Temperature | 380 to 420 | °C | |
| Nozzle Temperature | 370 to 410 | °C | |
| Processing (Melt) Temp | 370 to 410 | °C | |
| Mold Temperature | 140 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NA40 NL IH | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| AMTOPP SP12 | Inteplast Group | PP, Unspecified | AMTOPP |
| KEBATER® PBT BF250 | BARLOG plastics GmbH | PBT | KEBATER® |
| LUVOCOM® 1105-7670/BL | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| WELLAMID Nylon 6000 GV 50 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |