Sarlink AB-2140D is a high hardness thermoplastic elastomer designed for automotive interior applications. Sarlink AB-2140D can be processed by injection molding.

General Information
Features	Low density Impact resistance, high High hardness
Uses	Application in Automobile Field Car interior parts
Appearance	Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.898	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	11	g/10 min	ASTM D1238
Molding Shrinkage			ASTM D955
Flow : 80°C, 30 minutes	0.90	%	ASTM D955
Flow : 93°C, 30 minutes	1.2	%	ASTM D955
Flow : 80°C, 24 hours	0.90	%	ASTM D955
Transverse flow : 80°C, 24 hours	1.0	%	ASTM D955
Transverse flow : 80°C, 30 minutes	0.90	%	ASTM D955
Transverse flow : 93°C, 30 minutes	1.3	%	ASTM D955

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shore D, 1 second, injection molding	43	ASTM D2240
Shore D, 5 seconds, injection molding	40	ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus			ASTM D790
-30°C	2080	MPa	ASTM D790
23°C	150	MPa	ASTM D790
70°C	62.0	MPa	ASTM D790

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
Transverse flow : 100% strain	6.07	MPa	ASTM D412
Flow : 100% strain	7.42	MPa	ASTM D412
Tensile Strength			ASTM D412
Transverse flow : Yield	8.50	MPa	ASTM D412
Flow : Yield	9.00	MPa	ASTM D412
Tensile Elongation			ASTM D412
Transverse flow : Fracture	650	%	ASTM D412
Flow : Fracture	470	%	ASTM D412
Tear Strength - Across Flow ¹	62.0	kN/m	ASTM D624
Compression Set			ASTM D395
23°C, 22 hr	46	%	ASTM D395
70°C, 22 hr	81	%	ASTM D395

Impact	Nominal Value	Unit	Test Method
Instrumented Dart Impact			ASTM D3763
-40°C, peak load energy	22.4	J	ASTM D3763
23°C, peak load energy	18.4	J	ASTM D3763

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air - Across Flow			ISO 188
110°C, 1008 hr	0.0	%	ISO 188
125°C, 168 hr	-2.4	%	ISO 188
Changes in tensile stress upon fracture in air- Transverse flow			ISO 188
110°C, 1008 hr	-23	%	ISO 188
125°C, 168 hr	-32	%	ISO 188
Change in Shore Hardness in Air			ISO 188
Support d, 110°C, 1008 hr	1.1		ISO 188
Support d, 125°C, 168 hr	1.0		ISO 188

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	-60.0	°C	ASTM D746

Flammability	Nominal Value	Unit	Test Method
Burning Rate	25	mm/min	ISO 3795

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 206 sec^-1)	267	Pa·s	ASTM D3835

Additional Information
撕裂强度ASTM D624试验中所列的数值，依照ASTM D1004进行试验。模具收缩，线性变换，ASTM D955，80°C，30分钟：0.009英寸/英寸模具收缩，线性变换，ASTM D955，93°C，30分钟：0.013 英寸/英寸

Legal statement
The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Legal statement

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Injection	Nominal Value	Unit
Rear Temperature	199 - 210	°C
Middle Temperature	204 - 216	°C
Front Temperature	210 - 221	°C
Nozzle Temperature	216 - 227	°C
Processing (Melt) Temp	216 - 227	°C
Mold Temperature	35.0 - 65.6	°C
Injection Pressure	1.38 - 6.89	MPa
Injection Rate	Fast
Back Pressure	0.172 - 0.862	MPa
Screw Speed	50 - 120	rpm
Cushion	3.81 - 25.4	mm

Injection instructions
无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。

Note Message
1 .	C mould

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Sarlink® TPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PoedEF_Sarlink-TPE-AB-2140DN.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
VENYL SW108 - 7838	AD majoris	Nylon 6	VENYL
Halene P F135	Haldia Petrochemicals Ltd.	PP Homopolymer	Halene P
Kinta NI6600	Kinta Technology (Hong Kong) Co., Ltd.	Nylon 66	Kinta
LEXAN™ 940 resin	SABIC Innovative Plastics	PC	LEXAN™
SABIC® LLDPE M200024	Saudi Basic Industries Corporation (SABIC)	LLDPE	SABIC® LLDPE