Romiloy® 1015 ER
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PngtTg_Romiloy1015ER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®1015 ER is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in Europe, and the processing method is injection molding. Romiloy®The main features of 1015 ER are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 42 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 138 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA HD-L01 PLA Impact Modifier (Opaque) | Polyvel Inc. | PLA | Polyvel PLA |
| Spartech Polycom SCR1-5006 | Spartech Polycom | ABS | Spartech |
| AKROMID® A28 GF 50 1 GIT black (5029) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ALTECH® PA66 A 1000/109 YL2492-12LS | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| LEXAN™ HFD1262 resin | SABIC Innovative Plastics | PC | LEXAN™ |